| 引用本文: | 卞进田,叶庆,孙晓泉.ZnGeP2 OPO产生4.3 μm波段窄线宽激光实验研究.[J].国防科技大学学报,2018,40(4):9-14.[点击复制] |
| BIAN Jintian,YE Qing,SUN Xiaoquan.ZnGeP2 optical parametric oscillator 4.3 μm laser with narrow line-width[J].Journal of National University of Defense Technology,2018,40(4):9-14[点击复制] |
|
| |
|
|
| 本文已被：浏览 7963次 下载 6082次 |
| ZnGeP2 OPO产生4.3 μm波段窄线宽激光实验研究 |
| 卞进田, 叶庆, 孙晓泉 |
|
(国防科技大学 脉冲功率激光技术国家重点实验室， 安徽 合肥 230037)
|
| 摘要: |
| 为了设计4.3 μm波段大功率窄线宽中红外激光器，开展了2.7 μm激光抽运ZnGeP2晶体光参量振荡(Optical Parametric Oscillation, OPO)技术产生4.3 μm波段窄线宽激光实验研究，对实验结果开展了详细的分析。抽运源为1064 nm抽运的KTiOPO4 OPO激光器输出的2.7 μm波段参量激光，KTiOPO4 OPO采用单谐振结构，将两块相同的KTiOPO4晶体光轴相向放置以补偿走离效应，KTiOPO4晶体按Φ=0°、θ=62°切割以获得波长2.7 μm波段激光输出，采用Ⅱ(B)类相位匹配（o→o+e）以利用较大的非线性系数。ZnGeP2 OPO采用单谐振结构，采用Ⅱ(B)类相位匹配（o→o+e）以获得窄线宽输出，ZnGeP2晶体按Φ=0°、θ=68°切割以获得波长4.3 μm波段激光输出。在抽运光波长2.7 μm，脉冲能量为7.5 mJ，脉宽8.6 ns的条件下，获得脉冲能量2.12 mJ，线宽30 nm，脉宽8.7 ns的4.26 μm激光输出，光-光转换效率约为28.3%，斜效率约为32.6%，水平和垂直方向的光束质量M2分别为6.2和13.5。 |
| 关键词: 激光器 4.3 μm激光 单谐振光参量振荡器 ZnGeP2晶体 |
| DOI：10.11887/j.cn.201804002 |
| 投稿日期：2018-01-14 |
| 基金项目:脉冲功率激光技术国家重点实验室主任基金资助项目（KY13C162） |
|
| ZnGeP2 optical parametric oscillator 4.3 μm laser with narrow line-width |
| BIAN Jintian, YE Qing, SUN Xiaoquan |
|
(State Key Laboratory of Pulsed Power Laser Technology, National University of Defense Technology， Hefei 230037, China)
|
| Abstract: |
| In order to design high-power narrow line width 4.3 μm laser, the narrow line width 4.3 μm laser was obtained by ZnGeP2 OPO (optical parametric oscillation) pumped by a 2.7 μm laser. Experimental results were analyzed in detail. The pump source was a 2.7 μm KTiOPO4 OPO laser pumped by a 1064 nm Nd:YAG laser, and the KTiOPO4 OPO was singly resonated. Two identical KTiOPO4 crystals were placed with opposite optical axis to compensate the walk off effect. The KTiOPO4 crystals were cut asΦ=0°,θ=62° to generate 2.7 μm wave band laser. To utilize the large effective nonlinear coefficient, the phase matching was based on type Ⅱ(B) (o→o+e). The ZnGeP2 OPO was singly resonated too. To output narrow line width laser, the phase matching is based on typeⅡ(B) (o→o+e).The ZnGeP2 crystal was cut as Φ=0°,θ=68° to generate 4.3 μm laser. The energy of the 2.7 μm laser is 7.5 mJ with a pulse of 8.6 ns and line-width 12 nm.The pulse energy of 2.12 mJ at 4.26 μm with an optical-optical conversion efficiency of 28.3% and a slop efficiency of 32.6% is obtained, and the pulse width is 8.7 ns, the line-width is 30 nm. The beam qualities M2 of horizontal and vertical directions are 6.2 and 13.5, respectively. |
| Keywords: lasers 4.3 μm laser the single-resonant optical parametric oscillation ZnGeP2 crystal |
|
|