The Structure and Property of the Nanometer Si-C-N Reinforced Si3N4 Composites
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    本文用Si-C-N纳米微粉做增强相, Si3N4 微粉为基相, 采用热压的方法制备了SiCp/Si3N4 纳米复相陶瓷, 所得的SiCp/Si3N4 复合材料的室温弯曲强度为878.5MPa, 断裂韧性达11.96MPam1/2, 同时应用扫描电镜(SEM)、高分辨透射电镜(HRTEM) 对其结构进行了观察, 讨论了结构与性能之间的关系。

    Abstract:

    Nanometer composites are prepared by hot-pressing-sintering method in the paper, using nanometer Si-C-N particles as reinforce phase, Si3N4 as matrix phase, the bending strength of the materials reaches 878.5MPa and the fracture toughness reaches to 11.96 MPam1/2. The hot-pressed samples structure is characterized by scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) at the same time, the relationship between the structure and the property is discussed.

    参考文献
    相似文献
    引证文献
引用本文

周新贵,张长瑞,周安郴,等.纳米Si-C-N粒子增强Si3N4 复合材料的结构与性能[J].国防科技大学学报,1999,21(3):38-40.
Zhou Xingui, Zhang Changrui, Zhou Anchen, et al. The Structure and Property of the Nanometer Si-C-N Reinforced Si3N4 Composites[J]. Journal of National University of Defense Technology,1999,21(3):38-40.