| 引用本文: | 宋永才.高含钛量碳化硅纤维的研制.[J].国防科技大学学报,1989,11(2):101-106.[点击复制] |
| Song Yongcai.Development of SiC Fiber with High Molar Ratio of Ti/Si[J].Journal of National University of Defense Technology,1989,11(2):101-106[点击复制] |
|
| |
|
|
| 本文已被：浏览 5215次 下载 5468次 |
| 高含钛量碳化硅纤维的研制 |
| 宋永才 |
|
(材料科学与应用化学系)
|
| 摘要: |
| 本文采用一种聚钛硅氧烷与聚碳硅烷反应，制得了Ti/Si 摩尔比为 0.10 的聚钛碳硅烷。该聚合物具有良好的成丝性与稳定性，经熔融纺丝，再经不熔化处理后，在氮气气氛保护下1300℃热处理后制得了高含钛量的碳化硅纤维。文中对聚钛硅氧烷的合成与结构，它与聚碳硅烷的反应过程及聚钛碳硅烷的热分解特性进行了分析与研究。 |
| 关键词: 复合材料，聚铁硅氧烷，聚碳硅烷，聚钛碳硅烷，碳化硅纤维 |
| DOI： |
| 投稿日期：1988-04-02 |
| 基金项目: |
|
| Development of SiC Fiber with High Molar Ratio of Ti/Si |
| Song Yongcai |
|
(Department of Material Science and Applied Chemistry)
|
| Abstract: |
| The Polytitanocarbosilane with the molar ratio of Ti:Si=1:10 had been prepared by the reaction of polycarbosilane with polytitanosiloxane. This polymer had excellent spinnability and stability. After being melt spinning and unmelting treatment，followed by heat treatment at 1300℃ in the presence of nitrogen atmosphere，the SiC fiber with high molar ratio of Ti/Si was obtained. The synthesis and structure of cited polytitanosiloxane，its reaction process with polycarbosilane，and the pyrolytic properties of polytitanocarbosilane were examined and discussed. |
| Keywords: composite,polytitanosiloxane polycarbosilane,polytitanocarbosilane, SiC fiber |
|
|