| 引用本文: | 王跃.复合材料修补金属裂损结构吸湿老化的试验与有限元分析.[J].国防科技大学学报,2020,42(4):64-70.[点击复制] |
| WANG Yue.Experimental study and finite element analysis on hygroscopic aging of adhesively bonded composite repaired metallic structures with cracks[J].Journal of National University of Defense Technology,2020,42(4):64-70[点击复制] |
|
| |
|
|
| 本文已被：浏览 6491次 下载 5391次 |
| 复合材料修补金属裂损结构吸湿老化的试验与有限元分析 |
| 王跃 |
|
(空军研究院, 北京 100085)
|
| 摘要: |
| 暴露在湿热环境中的复合材料修补金属裂损结构易吸湿老化,导致该结构性能下降,服役寿命缩短。为研究吸湿性对复合材料修补金属裂损结构修补效果和耐久性的影响,利用试验方法分析了吸湿性对复合材料胶补金属裂损结构及胶黏剂力学性能的影响；利用有限元方法评估了吸湿性对复合材料胶补金属裂损结构试验件修补效果和耐久性的影响。研究结果表明:吸湿后含穿透双边裂纹铝合金板玻璃纤维单面胶补试验件的疲劳裂纹扩展寿命和极限载荷的平均值分别下降为吸湿前的71%和90%；吸湿造成拉伸条件下复合材料胶补金属裂损结构胶层失效模式由内聚破坏为主转变为界面破坏为主；在“湿-热”老化30天后,E44/聚酰胺环氧树脂胶黏剂试验件吸水饱和,弹性模量下降为未老化前的40%,塑性应变超过了总应变的25%；有限元分析发现胶层损伤受吸湿影响明显,吸湿性加速了胶层损伤,且裂纹长度越长,加速作用越明显；同时吸湿使得裂纹尖端的J积分值急剧增大,导致修补结构的疲劳裂纹扩展寿命缩短,裂纹长度越长,吸湿性对于复合材料胶接修补效果的危害越严重。 |
| 关键词: “湿-热”老化试验 吸湿性 复合材料单面胶补 损伤区域理论 J积分 |
| DOI：10.11887/j.cn.202004011 |
| 投稿日期：2018-11-27 |
| 基金项目: |
|
| Experimental study and finite element analysis on hygroscopic aging of adhesively bonded composite repaired metallic structures with cracks |
| WANG Yue |
|
(Air Force Research Institute, Beijing 100085, China)
|
| Abstract: |
| Due to serve under the environment of high temperature and high humidity, hygroscopic aging behaviors are commonly discovered in adhesively bonded composite repaired metallic aircraft structures, which results in the decrease in mechanical properties and server life. In order to investigate the effect of hygroscopic aging on adhesively bonded composite repaired structures, moisture absorption and aging test were performed on adhesively bonded composite repaired aluminum alloys plates containing double-sides cracks with single patch and E44/Polyamide epoxy resin, then the effect of hygroscopic aging on load carrying capability, crack propagation life, repaired effect and duration of fatigue load were analyzed by the experimental method and finite element method (including damage zone theory and J-integral ). Results show that hygroscopic aging lowers the load carrying capability and fatigue crack propagation life greatly, with the result that the average value of fatigue crack propagation life and ultimate load of repaired structure decreases by 29% and 10% respectively after immersing in water for 40 days, and the failing mode of adhesive changes into interfacial failure from cohesive failure. After immersing in water for 30 days, the adhesive specimens became completely plastic, whose elastic module decreases by 60%, and plastic deformation increases to 25%. The effect of hygroscopic aging on the damage zone was obvious, which results in the fast damage of adhesive, and the longer the crack is, the faster the damage is. The hygroscopic aging of repaired structure also increases the value of J-integral around the crack tips, which decreases the crack propagation life of repaired structures. |
| Keywords: hydrothermal aging test hygroscopic property adhesively bonded composite repair damage zone theory J-integral |
|
|
|
|
|